Property |
Unit |
Test Method |
Test Condition |
Data |
|
Specific gravity |
g/cm3 |
ISO1183 |
|
1.29 |
|
MRF |
g/10min |
ISO1133 |
230°C/2.16kg |
4.7 |
|
Tensile strength |
MPa |
ISO527-1/-2 |
|
53.8±0.76 |
|
Tensile strain |
MPa |
ISO527-1/-2 |
|
2,660±63 |
|
Breaking Elongation |
% |
ISO527-1/-2 |
|
22.6±0.44 |
|
Flexural strength |
MPa |
ISO178 |
|
70.3±2.6 |
|
Flexural modulus |
MPa |
ISO178 |
|
2,280±150 |
|
Izod impact strength |
kJ/m2 |
ISO179-1 |
|
321±65 |
|
Impact strength (Notched) |
kJ/m2 |
ISO179-1 |
|
3.53±2 |
|
HDT |
°C |
ISO75-1/-2 |
|
89.8 |
|
Rockwell hardness |
R-scale |
ISO2039-2 |
|
109 |
|
Shrinkage from molding |
% |
ASTM D955 |
|
0.3-0.5 |
|
|
Unit |
Parameter |
|
Pre-drying |
°C, hours |
70°C, 4hours |
|
Thermoprofiles |
°C |
|
|
Feeding zone |
°C |
210-230 |
|
Barrel |
°C |
210-230 |
|
Die |
°C |
210-230 |